high speed steel sheets




        Inquiry   Now      
        Contact   Info       
   
   


high speed steel sheets W2Mo9Cr4VCo8(M42)

Specification: Hot-rolled steel sheet Thickness 2.5-10.5mm

Width 800mm

Length 1500-2000mm

Cold -rolled steel sheet Thickness 1.0-2.5mm

Width 750mm

Length 1500-2000mm



Delivery Condition: Annealed hardness HB≤255

Package: Suitable for export



The detailed material we could offer:

1. W6Mo5Cr4V2 , it is similar to M2( ASTM), S6-5-2(DIN), SKH51(JIS)

Chemical Composition: C 0.85, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 6.00, Mo 4.80 V 1.85

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1210-1230 Temperings 550

Secondary 63-65 HRC

Application: Be used widely in making all kinds of knives and durable cold working molds



2. W6Mo5Cr4V2Co5 , it is similar to M35( ASTM), 1.3243(DIN), SKH35(JIS)

Chemical Composition: C 0.93, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 6.30, Mo 4.80 V 1.85, Co 5.00

Annealed Hardness: HB≤269

Heat treatment temp: Hardening 1200-1220 Temperings 550

Secondary 64-67 HRC

Application: Steel for difficult and hi-speed cutting blades, blades which lay particular on durable



3. W2Mo9Cr4VCo8 , it is similar to M42 ( ASTM), 1.3247(DIN), SKH59(JIS)

Chemical Composition: C 1.10, Si 0.55, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 1.50, Mo 9.50 V 1.05, Co 8.00

Annealed Hardness: HB≤269

Heat treatment temp: Hardening 1210-1230 Temperings 550

Secondary 65-67 HRC

Application: Steel for difficult and hi-speed cutting blades, blades which lay particular on toughness



4. W18Cr4V , it is similar to T1 ( ASTM), 1.3355(DIN), SKH2(JIS)

Chemical Composition: C 0.75, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 4.05, W18, V 1.10

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1270-1285 Temperings 560

Secondary 62-65 HRC

Application: Steel for common cutting blades



5. W9Mo3Cr4V

Chemical Composition: C 0.83, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 4.05, W 8.90, Mo 2.90 V 1.45

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1220-1240 Temperings 550

Secondary 63-65 HRC

Application: Chinese material, similar capability to M2



6. W6Mo5Cr4V2Co(GB), it is equal to M2 modify ( ASTM)

Chemical Composition: C 0.80, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 5.40, Mo 4.80 V 2.10, Co≤0.5

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1200-1220 Temperings 550

Secondary 62-64 HRC

Application: Better toughness than M2




Zhejiang Guoli Tools Co.,Ltd Products

high speed steel sheets
high speed steel sheets W2Mo9Cr4VCo8(M42) Specification: Hot-rolled steel sheet Thickness 2.5-10.5mm Width 800mm Length 1500-2000mm Cold -rolled steel sheet Thickness 1.0-2.5mm...,high speed steel sheets, steel sheets,steel plates,hot rolled steel plates
 
planer knife
1. Made of high-quality 2. Sharp edge, high precision and long working life 3.Good quality and fast delivery ,planer knife , planer knife
 
high speed steel round bar
high speed steel round bar Hot rolling round bar: Diameter 8mm---32mm Precisely-forged round bar: Diameter 50mm --- 220mm Delivery Condition: Annealed or Ground Package: Suitable for export The detailed material we could offer: 1. 4Cr5MoSiV1 (GB) it is similar...,high speed steel round bar, round bar
 
 
Contact Info
URL:
TEL:
Fax:
Country: China
Address:
no.159 xinggong road hu town jinyun county lishui

Send Inquiry

 
Company:
*Contact:
*Email:
URL:
TEL:
Fax:
Country:
Address:
*Subject:
Comment:
 

 
 
 
  Contact Us Site Map About Us Trade Links
2005-2014 copyright by twfta.com. All rights reserved.